ASTM A453/A453M-10e1

Historical Revision

Standard Specification for High-Temperature Bolting, with Expansion Coefficients Comparable to Austenitic Stainless Steels

$83.00

$83.00

$149.40


Sub Total (1 Item(s))

$ 0.00

Estimated Shipping

$ 0.00

Total (Pre-Tax)

$ 0.00


...

1.1 This specification covers five grades of bolting with twelve classes of yield strength ranging from 50 to 120 ksi [345 to 827 MPa] for use in high-temperature service such as fasteners for pressure vessel and valve flanges. See Specification for the definition of bolting. The material requires special processing and is not intended for general purpose applications.

1.2 The following referenced general requirements are indispensable for application of this specification: Specification .

1.3 Supplementary Requirements are provided for use at the option of the purchaser. The Supplementary Requirements shall only apply when specified individually by the purchaser in the purchase order or contract.

1.4 This specification is expressed in both inch-pound units and in SI units; however, unless the purchase order or contract specifies the applicable M specification designation (SI units), the inch-pound units shall apply.

1.5 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.


This specification covers standards for Grade 660 (Class A, B, C, and D) , Grade 651 (Class A and B), Grade 662 (Class A and B), and Grade 665 (Class A and B) of bolting materials for use in high-temperature service such as fasteners, for pressure vessels and valve flanges. Bolting materials in this specification covers rolled, forged, or hot-extruded bars, and also bolts, nuts, screws, washers, studs, and stud bolts. Materials shall adhere to specified contents of carbon, manganese, phosphorus, sulfur, silicon, nickel, chromium, molybdenum, tungsten, titanium, columbium, aluminum, vanadium, boron, and copper. Materials shall be subjected to tension, stress-rupture, and hardness tests. Materials shall conform to yield strength, tensile strength, elongation, reduction of area, Brinell hardness, and Rockwell hardness requirements. Hardening and solution treatment requirements for each material class are also given.


SDO ASTM: ASTM International
Document Number A453
Publication Date April 1, 2010
Language en - English
Page Count 7
Revision Level 10e1
Supercedes
Committee A01.22
Publish Date Document Id Type View
May 1, 2017 A0453_A0453M-17 Revision
May 1, 2016 A0453_A0453M-16 Revision
Nov. 1, 2015 A0453_A0453M-15 Revision
May 1, 2012 A0453_A0453M-12 Revision
Nov. 1, 2011 A0453_A0453M-11 Revision
April 1, 2010 A0453_A0453M-10E01 Revision
April 1, 2010 A0453_A0453M-10 Revision
Oct. 1, 2008 A0453_A0453M-08 Revision
Oct. 1, 2004 A0453_A0453M-04 Revision
Oct. 1, 2003 A0453_A0453M-03 Revision
March 10, 2002 A0453_A0453M-02 Revision
March 10, 2002 A0453_A0453M-00E01 Revision
March 10, 2002 A0453_A0453M-00 Revision
March 1, 2024 A0453_A0453M-17R24 Reaffirmation